ElektroPhysik - Digital Coating Thickness Gauges - MiniTest 650
Overview
Application
Non-destructive coating thickness measurement:
-
Non-magnetic coatings like varnishes, enamels, chrome and zinc on ferromagnetic base materials (e.g. steel)
-
Insulating coatings like varnishes and anodising aluminium on non-ferrous metals (e.g. aluminium, copper, die-cast zinc)
Characteristics
-
Coating thickness measurement of up to 2 and 3 mm
-
Universal probe offering automatic substrate identification for quick measurement on steel and non-ferrous metals
-
Wear-resistant probe tips with practically unlimited durability
-
USB-interface to transfer data to a PC
-
Statistical evaluation of the readings (measurement data)
Scope of delivery
-
Gauge MiniTest 650 with fixed probe
-
3 batteries AAA / LR03 / Micro
-
Control plate(s), calibration standards in folding case
-
Operating manual on a CD
-
Quick reference guide
-
Factory certification
-
Soft case
Technical Details
|
Property |
Value |
|
Measuring range |
|
model F (steel): |
0 µm - 3000 µm / 120 mils |
|
model N (non-ferrous metal): |
0 µm - 2000 µm / 80 mils |
|
model FN (dual sensor): |
0 µm - 2000 µm / 80 mils |
|
|
Measuring uncertainty |
± (2 % of reading + 2 μm / 0.08 mils) |
|
Minimum curvature radius |
|
|
Minimum measuring area |
Ø 20 mm / |
|
Minimum base thickness |
|
F sensor: |
0.5 mm / |
|
N sensor: |
50 µm / |
|
|
Display |
4-digit screen data (11 mm / 0.44”) |
|
Measuring units |
μm – mils, user selectable |
|
Calibration |
standard, 1-point and 2-point calibration |
|
Statistics |
calculated from maximum 9.999 readings
- mean value
- standard deviation
- number of readings
- minimum
- maximum
|
|
Interface |
USB |
|
Power supply |
3 Micro AAA batteries (for more than 10,000 readings) |
|
Dimensions and weight |
|
gauge: |
70 mm x 122 mm x 32 mm / 2.7” x 4.8” x 1.26” |
|
sensor: |
Ø 15 mm x 62 mm / Ø 0.60” x 2.44” |
|
225 grams / 7.93 ozs |
|
|
Ambient temperature |
|
gauge: |
0 °C - 50 °C |
/ |
32 °F - 122 °F |
|
sensor: |
-10 °C - 70 °C |
/ |
14 °F - 158 °F |
|